Nitrogen Laser Mirrors
Substrate material: UV fused silica or BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Wedge: <3 are min.
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 1j/cm2  10nsec Pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

He-Cd Laser Mirrors
Substrate material: UV fused silica or BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 1j/cm2  10nsec Pulse
Adhesion Threshold: Per MIL-C-675A
Copper Vapoor Laser Mirrors
Substrate material: UV fused silica, CaF2 or BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 15-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 1 j/cm2  10nsec pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

He-Ne Laser Mirrors (632.8nm)
Substrate material: UV fused silica, BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 15-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold:  > 1 j/cm2  10nsec pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

Ruby Laser Mirrors (694.3nm)
Substrate material: UV fused silica, BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 15-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: > 10 j/cm2  10nsec pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

Alexandrite Laser Mirrors (720-780nm)
Substrate material: UV fused silica, BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: > 10 j/cm2  10nsec pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

Diode Laser Mirrors
Substrate material: BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Minimum Reflectance: ≥99%
Adhesion Threshold: Per MIL-C-675A
Forsterite (1235nm), Iodine (1315nm) Laser Mirrors
Substrate material: UV fused silica or BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 1 j/cm2  10ns pulse
Adhesion Threshold: Per MIL-C-675A
Er:Glass Laser Mirrors
Substrate material: BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 5 j/cm2  10ns pulse
Adhesion Threshold: Per MIL-C-675A

How To Order

Tm:YAG (2010nm) , Ho:YAG (2100nm) Laser Mirrors
Substrate material: BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: 10 j/cm2  10ns pulse
Adhesion Threshold: Per MIL-C-675A
Er:YAG Laser Mirrors (2940nm)
Substrate material: BK7
S1 Surface Figure: λ/10 @ 633nm
S1 Surface Quality: 10-5 laser quality
S2 Surface Quality: Commercial Polish
Diameter Tolerance: +0.0/-0.20 mm
Thickness Tolerance: ±0.25 mm
Clear Aperture: >85% of diameter
Chamfer: 0.3mm at 45 typical
Damage Thredold: >10 j/cm2  10ns
Adhesion Threshold: Per MIL-C-675A

How To Order